Ttulo [PT]: Compsitos de madeira/poliuretano a partir de resduos de madeira epoliol proveniente da reciclagem qumica do PET
Autor(es): Mrcia Fornasieri Domingos
Palavras-chave [PT]:

Compsitos de madeira/poliuretano. Reciclagem qumica do PET. Produo de poliois. Poliol. Resduos de madeira. Reaproveitamento. Madeira. Modificao qumica. Macerao e mercerizao. Compsitos matriz polimrica. Poliuretana. Reciclagem de madeira. Brasil.
Palavras-chave [EN]:
Polymer-matrix composites. PET. Polyurethane. Wood. Recycling. Brazil.
rea de concentrao: Qumica
Titulao: Mestre em Qumica
Banca:
Edvani Curti Muniz [Orientador] - UEM
Gizilene Maria de Carvalho - UEM
Rosana Maria Nascimento de Assuno - UFU
Resumo:
Resumo: Foram sintetizados compsitos de madeira/poliuretano utilizando poliois provenientes da reciclagem qumica do poli(etileno tereftalato) - PET, poliis comerciais e resduos de madeira provenientes de industrias moveleiras do Norte do Paran. A madeira foi quimicamente modificada em soluo de cido peractico (macerao) e de NaOH (mercerizao) para promover a adeso entre as fases. Para o preparo dos compsitos utilizou-se diferentes propores de resduos de madeira macerada (0-25% m/m) e quantidades fixas dos poliis e do tolueno diisocianato - TDI. Para caracterizao das modificaes qumicas ocorridas na madeira e dos compsitos foram utilizadas tcnicas de infravermelho (FTIR-PAS) e microscopia eletrnica de varredura (MEV), anlise trmica (TGA e DSC). Os compsitos tambm foram analisados atravs de ensaio mecnico de trao e difrao de raio-X de alto ngulo (WAXD). Observou-se por FTIR e por MEV que a modificao qumica da madeira utilizando o cido peractico permite a produo de compsitos com boa aderncia entre as fases. Atravs das analises de FTIR dos compsitos, observamos que com o aumento da quantidade de madeira nos compsitos, ocorreu um aumento dos grupos N-H ligados caracterizando a interao entre poliuretano e a madeira. O aumento do mdulo de elasticidade e o decrscimo da deformao na ruptura com o aumento de proporo de madeira nos compsitos indicam que a transferncia de carga da matriz para a fase dispersa efetiva. Os resultados de TGA indicam que a estabilidade trmica dos compsitos superior a do polmero puro. Podemos inferir que a utilizao de resduos de madeira e poliol obtido da reciclagem qumica do PET na produo de compsitos com resina poliuretana uma alternativa de grande viabilidade, constituindo uma opo na preservao do meio ambiente.

Abstract: Polyol/wood composites were synthesized with wood residues from furniture companies of the north of Paran State and polyols obtained from chemically recycled poly(ethylene terephthalate) (PET) and commercial polyols. Wood was chemically modified (maceration) with peracetic acid and (mercerization) with NaOH to promote phase adhesion. Composites were prepared with different proportions of macerated wood residues (0-25% m/m) and fixed amounts of polyols and diisocyanate toluene (TDI). The chemically modified wood and composites were characterized by infrared spectroscopy (FTIR-PAS), scanning electron microscopy (SEM), and thermal analysis (TGA and DSC). The composites were also analysed by tensile strength and wide angle X-ray diffraction (WAXD). FTIR and SEM analyses of wood showed that the chemical modification with peracetic acid resulted in composites with good phase adherence. The FTIR analysis of the composites show that as the amount of wood in the composites increased, an increase of the N-H linked groups occurred as well, which characterizes an interaction between the polyurethane and the wood. The increase in the Young's modulus and the decrease of elongation at break with the increase in the proportion of wood in the composites indicates effective load transfer from the matrix to the dispersed phase. According to the TGA results, the composites are thermally more stable than the pure polymer. It is possible to infer that the utilization of wood residues and polyol, obtained from the chemical recycling of PET, during the production of composites wood-polyurethane resin is a very feasible alternative, which is an option when the preservation of the environment is considered.
Data da defesa: 12/03/2010
Cdigo: vtls000183932
Informaes adicionais:
Idioma: Portugus
Data de Publicao: 2010
Local de Publicao: Maring, PR
Orientador: Prof. Dr. Adley Forti Rubira
Instituio: Universidade Estadual de Maring. Departamento de Qumica
Nvel: Dissertao (mestrado em Qumica)/
UEM: Programa de Ps-Graduao em Qumica

Responsavel: beth
Categoria: Aplicao
Formato: Documento PDF
Arquivo: Marcia Fornasieri Domingos - Dissertacao.pdf
Tamanho: 1827 Kb (1871149 bytes)
Criado: 03-05-2011 10:06
Atualizado: 19-03-2018 14:32
Visitas: 1146
Downloads: 24

[Visualizar]  [Download]

Todo material disponvel neste sistema de propriedade e responsabilidade de seus autores.

Voltar