Biblioteca Digital da UEM: Sistema Nou-Rau
Pgina Principal  Portugus   English  Español   Aumentar Texto  Texto Normal  Diminuir Texto
  Principal | Apresentao | Objetivos | Instrues Autores | Estatsticas | Outras Bibliotecas Digitais
  Sistema Integrado de Bibliotecas - SIB / UEM
Entrar | acessos | verso 1.1  
ndice
Pgina principal
Documentos
Novidades
Usurios

Aes
Consultar
Procurar
Exibir estatsticas

Procurar por:
Procura avanada

Dvidas e sugestes


Consultar: Programa de Ps-Graduao em Fsica (Acadmico)

Incio > Dissertaes e Teses > Cincias Exatas e da Terra > Fsica > Programa de Ps-Graduao em Fsica (Acadmico)

Ttulo [PT]: Desenvolvimento de sensores de gases base de Fe-Bi2O3
Autor(es): Rosimeire Bemvides Zampiere
Palavras-chave [PT]:

Sensor de gs. Termoeletroresistometria. Moagem de alta energia. Magnetizao. Raios X.
Palavras-chave [EN]:
Gas sensor. Thermoelectroresistometry. High energy ball mill. Magnetization. X ray.
rea de concentrao: Fsica da Matria Condensada
Titulao: Mestre em Fsica
Banca:
Suzana Nbrega de Medeiros [Orientador] - UEM
Luiz Fernando Ctica - UNICENTRO
Antonio Medina Neto - UEM
Resumo:
Resumo: Compsitos metal-cermicos foram sintetizados via moagem de alta energia, a partir de ferro metlico (α Fe) e xido de bismuto (Bi2O3), variando-se a concentrao nominal relativa e usando-se dois moinhos diferentes. Os produtos da moagem foram caracterizados por difratometria de raios X, espectroscopia Mssbauer e medidas de magnetizao em funo do campo magntico aplicado. As amostras de Fex(Bi2O3)1-x (x ≤0,40), preparadas atravs do moinho planetrio, revelaram a formao das fases BiFeO3 e Bi25FeO40. Para as amostras com x > 0,40, observa-se uma estrutura desordenada e a formao da fase Bi25FeO40, alm de Fe e Bi. Os espectros Mssbauer para essas amostras (x = 0,50 e x = 0,60) foram ajustados com um sexteto (α Fe) e um dubleto atribudo fase Bi25FeO40. As curvas de magnetizao por campo obtidas so caractersticas de um sistema que apresenta superparamagnetismo em conjunto com uma pequena frao de ferromagnetismo. J, para o moinho vibratrio, os resultados mostraram que a fase Bi25FeO40 a nica fase obtida para todas as amostras entre 0,05 ≤ x ≤ 0,20. As medidas do sistema de termoeletroresistometria mostraram que a fase Bi25FeO40 sensvel ao gs metano (CH4) e dixido de carbono (CO2).

Abstract: Metal-oxide composites were synthesized in high-energy ball-milling of metallic iron (α Fe) and bismuth oxide (Bi2O3) powders, varying the starting relative concentration and using two different mills. The samples were characterized by X-ray diffraction, Mssbauer spectroscopy and magnetization versus field measurements. For the Fex(Bi2O3)1-x (x ≤ 0,40) samples, prepared in a planetary mill, the results reveled the formation of the BiFeO3 and Bi25FeO40 phases. For x > 0,40, was observed the formation of a disordered structure, Bi25FeO40, Bi and Fe phases. The Mssbauer spectrum for this samples (x = 0,50 and x = 0,60) was fitted with a sextet (α Fe) and a doublet assigned to the Bi25FeO40 phase. The obtained magnetization versus field loops are characteristic of a system exhibiting superparamagnetism together with a small magnetically ordered fraction attributed to iron precipitates. In the case of shaker mill, the results showed that Bi25FeO40 phase is the main phase in all the samples (0,05 ≤ x ≤ 0,20). Thermoelectroresistometry measurement showed that Bi25FeO40 phase is sensitive to methane gas (CH4) and carbon dioxide (CO2).
Data da defesa: 30/02/2008
Cdigo: vtls000169252
Informaes adicionais:
Idioma: Portugus
Data de Publicao: 2008
Local de Publicao: Maring
Orientador: Prof. Dr. Suzana Nbrega de Medeiros
Instituio: Universidade Estadual de Maring. Departamento de Fsica Nvel: Dissertao (mestrado em Fsica)/
UEM: Programa de Ps-Graduao em Fsica

Responsavel: inez
Categoria: Aplicao
Formato: Documento PDF
Arquivo: rosimeire_bemvides_zampiere_2008.pdf
Tamanho: 3562 Kb (3647655 bytes)
Criado: 12-11-2009 14:30
Atualizado: 12-11-2009 14:47
Visitas: 998
Downloads: 24

[Visualizar]  [Download]

Todo material disponvel neste sistema de propriedade e responsabilidade de seus autores.