Biblioteca Digital da UEM: Sistema Nou-Rau
Pgina Principal  Portugus   English  Español   Aumentar Texto  Texto Normal  Diminuir Texto
  Principal | Apresentao | Objetivos | Instrues Autores | Estatsticas | Outras Bibliotecas Digitais
  Sistema Integrado de Bibliotecas - SIB / UEM
Entrar | acessos | verso 1.1  
ndice
Pgina principal
Documentos
Novidades
Usurios

Aes
Consultar
Procurar
Exibir estatsticas

Procurar por:
Procura avanada

Dvidas e sugestes


Consultar: Programa de Ps-Graduao em Engenharia Mecnica

Incio > Dissertaes e Teses > Engenharias > Engenharia Mecnica > Programa de Ps-Graduao em Engenharia Mecnica

Ttulo [PT]: Sntese e determinao do mdulo elstico de cermicas de 0,6BiFeO3-0,4PbTiO3 dopadas com La
Autor(es): Cecilia Irene Berveglieri
Palavras-chave [PT]:

Mdulo elstico. Tcnica de excitao por impulso. Piezeltrico. Brasil.
Palavras-chave [EN]:
Elastic Modulus. Impulse Excitation Technique. Piezoeletric. Brazil.
Titulao: Mestre em Engenharia Mecnica
Banca:
Ivair Aparecido dos Santos [Orientador] - UEM
Silvia Luciana Fvaro Rosa - UEM
Valdirlei Fernandes Freitas - UNICENTRO
Resumo:
Resumo: O Mdulo Elstico de um material um parmetro fundamental para a engenharia e aplicao de materiais, pois est associado a outras propriedades mecnicas como tenso de escoamento e tenso de ruptura. A avaliao desse parmetro para o composto de ferrita de bismuto e titanato de chumbo torna-se importante uma vez que em aplicaes piezeltricas os dispositivos trabalham dentre do regime elstico. Neste trabalho, amostras cermicas de 0,6BiFeO3-0,4PbTiO3 dopadas com 3, 5 e 10% de La em massa foram processadas por moagem em altas e baixas energias e sinterizao ao ar, nas temperaturas de 1015, 1065 e 1115 C por 1 h. Seus Mdulos Elsticos foram determinados por meio da Tcnica de Excitao por Impulso. A Tcnica de Excitao por Impulso uma tcnica no destrutiva para avaliao das propriedades elsticas e de amortecimento dos materiais. Os resultados mostraram um Mdulo Elstico mximo de 74 GPa para a amostra dopada com 3% de lantnio e sinterizada 1115 C. Para todas as amostras foi observado o aumento do Mdulo Elstico com o aumento da temperatura de sinterizao, com consequente diminuio dessa propriedade com o aumento da concentrao de lantnio.

Abstract: The Elastic Modulus is a key parameter for engineering and application of materials; and is associated with other mechanical properties, such as yield stress and rupture stress. The assessment of this parameter for the compound of bismuth ferrite and lead titanate becomes important since the application of piezoelectric devices work in the elastic regime. In this study, 3, 5 and 10% of La doped 0.6BiFeO3-0.4PbTiO3 ceramics were processed through high and low-energy ball milling, followed by sintering in air at 1015, 1065 and 1115 C for 1 h. Their Elastic Moduli were determined by the Impulse Excitation Technique. The Impulse Excitation Technique (IET) is a non-destructive technique for evaluation of the elastic and damping properties of materials. The results showed a maximum elastic modulus of 74 GPa to 3% doped with lanthanum and sintered at 1115 C. For the other samples, it was observed an increase of the Elastic Modulus with the temperature increasing, with a consequent decrease of this property with the increase of lanthanum content.
Data da defesa: 26/08/2015
Cdigo: vtls000220372
Informaes adicionais:
Idioma: Portugus
Data de Publicao: 2015
Local de Publicao: Maring, PR
Orientador: Prof. Dr. Ivair Aparecido dos Santos
Instituio: Universidade Estadual de Maring . Centro de Tecnologia . Programa de Ps-Graduao em Engenharia Mecnica
Nvel: Dissertao (mestrado em Engenharia Mecnica)/
UEM: Departamento de Engenharia Mecnica

Responsavel: beth
Categoria: Aplicao
Formato: Documento PDF
Arquivo: Berveglieri,C.I_Dissertao.pdf
Tamanho: 1705 Kb (1745720 bytes)
Criado: 08-10-2016 09:43
Atualizado: 08-10-2016 09:46
Visitas: 305
Downloads: 63

[Visualizar]  [Download]

Todo material disponvel neste sistema de propriedade e responsabilidade de seus autores.